Development of Antibacterial Resin Composites Incorporating Poly(METAC) Clusters.

This study examined the antibacterial effects and physical properties of a novel resin composite incorporating poly[{2-(methacryloyloxy)ethyl}trimethylammonium chloride] (poly(METAC)), a methacrylate cationic polymer comprising quaternary ammonium compounds (QACs). Resin composites incorporating poly(METAC) were fabricated by adding 6 wt.% METAC aqueous solution to a commercially available resin composite. The FE-SEM/EDS and Raman spec-troscopy analyses showed that METAC was assembled and polymerized in the resin composites after curing. The antibacterial effect was evaluated by inoculating Streptococcus mutans or Strepto-coccus sobrinus suspensions on the surface of cured resin composites, and the experimental resin composites incorporating poly(METAC) clusters exhibited bactericidal effects even after 28 days of ageing. The physical properties of the experimental resin composites were within the ISO-stipulated ranges. Newly fabricated resin composites containing the QAC-based poly(METAC) cluster ex-hibited long-term bactericidal effects against oral bacteria on their surfaces and demonstrated ac-ceptable physical properties for clinical use.

CAD-CAM resin composites: Effective components for further development.

OBJECTIVE: This paper summarizes the effective components of computer-aided design and computer-aided manufacturing (CAD-CAM) resin composites that contribute to achieving greater mechanical properties and further development. METHODS: In silico multi-scale analysis, in silico nonlinear dynamic finite element analysis (FEA), and artificial intelligence (AI) were used to explore the effective components of CAD-CAM resin composites. The effects of the filler diameter and silane coupling ratio on the mechanical properties of CAD-CAM resin composites have been clarified through multi-scale analysis. The effects of the filler contents, and filler and monomer compositions have been investigated by AI algorithms. The fracture behavior of CAD-CAM composite crown was analyzed using in silico non-linear dynamic FEA. The longevity of CAD-CAM composite crown was assessed through step-stress accelerating life testing (SSALT). RESULTS: As the filler diameter decreases, there is an increase in elastic moduli and compressive strengths at the macroscale. At the nanoscale, a decrease in the filler diameter results in a decrease in the maximum value of the maximum principal strain. When the silane coupling ratio decreases, there is a decrease in the elastic modulus and compressive strength. According to the exhaustive search and feature importance analysis based on the AI algorithm, the combination of certain components was narrowed down to achieve a flexural strength of 269.5 MPa. The in silico non-linear FEA successfully detected the sign of the initial crack of the CAD-CAM composite molar crown. The SSALT revealed that CAD-CAM resin composite molar crowns containing nanofillers with a high fraction of resin matrix demonstrated great longevity. SIGNIFICANCE: This paper summarized the effective components of CAD-CAM resin composites for their further development. The integration of in vitro and in silico approaches will expedite the advancement of CAD-CAM resin composites, offering benefits such as time efficiency and reduction of material waste for researchers and manufacturers.

Poly(lactic acid/caprolactone) bilayer membrane achieves bone regeneration through a prolonged barrier function.

Guided bone regeneration (GBR) is a treatment strategy used to recover bone volume. Barrier membranes are a key component of GBR protocols, and their properties can impact treatment outcomes. This study investigated the efficacy of an experimental, slow-degrading, bilayer barrier membrane for application in GBR using in vivo animal models. A synthetic copolymer of poly(lactic acid/caprolactone) (PLCL) was used to prepare a slow-degrading bilayer membrane. The biodegradability of PLCL was evaluated by subcutaneous implantation in a rat model. The barrier function of the PLCL membrane was investigated in a rat calvaria defect model and compared with commercially available membranes composed of type I collagen (Col) and poly(lactic-co-glycolic acid) (PLGA). An alveolar bone defect model in beagle dogs was used to simulate GBR protocols to evaluate the bone regeneration ability of the experimental PLCL membrane. The PLCL membrane showed slow biodegradation, resulting in an efficient and prolonged barrier function compared with commercial materials. In turn, this barrier function enabled the space-making ability of PLCL membrane and facilitated bone regeneration. In the alveolar bone defect model, significantly greater regeneration was achieved by treatment with PLCL membrane compared with Col and PLGA membranes. Additionally, a continuous alveolar ridge contour was observed in PLCL-treated bone defects. In conclusion, the PLCL bilayer membrane is a promising biomaterial for use in GBR given its slow degradation and prolonged barrier function.

Multiple-Ion Releasing Bioactive Surface Pre-Reacted Glass-Ionomer (S-PRG) Filler: Innovative Technology for Dental Treatment and Care.

Surface Pre-Reacted Glass-ionomer (S-PRG) filler, which releases strontium (Sr2+), borate (BO33-), fluoride (F-), sodium (Na+), silicate (SiO32-), and aluminum (Al3+) ions at high concentrations, is a unique glass filler that are utilized in dentistry. Because of its multiple-ion releasing characteristics, S-PRG filler exhibits several bioactivities such as tooth strengthening, acid neutralization, promotion of mineralization, inhibition of bacteria and fungi, inhibition of matrix metalloproteinases, and enhancement of cell activity. Therefore, S-PRG filler per se and S-PRG filler-containing materials have the potential to be beneficial for various dental treatments and care. Those include restorative treatment, caries prevention/management, vital pulp therapy, endodontic treatment, prevention/treatment of periodontal disease, prevention of denture stomatitis, and perforation repair/root end filling. This review summarizes bioactive functions exhibited by S-PRG filler and its possible contribution to oral health.

Fabrication of pH-Responsive Zn2+-Releasing Glass Particles for Smart Antibacterial Restoratives.

The on-demand release of antibacterial components due to pH variations caused by acidogenic/cariogenic bacteria is a possible design for smart antibacterial restorative materials. This study aimed to fabricate pH-responsive Zn2+-releasing glass particles and evaluate their solubilities, ion-releasing characteristics, and antibacterial properties in vitro. Three kinds of silicate-based glass particles containing different molar ratios of Zn (PG-1: 25.3; PG-2: 34.6; PG-3: 42.7 mol%) were fabricated. Each particle was immersed in a pH-adjusted medium, and the solubility and concentration of the released ions were determined. To evaluate the antibacterial effect, Streptococcus mutans was cultured in the pH-adjusted medium in the presence of each particle, and the bacterial number was counted. The solubility and concentration of Zn2+ released in the medium increased with a decrease in medium pH. PG-3 with a greater content of Zn demonstrated higher concentrations of released Zn2+ compared with PG-1 and PG-2. PG-2 exhibited bactericidal effects at pH 5.1, whereas PG-3 demonstrated bactericidal effects at pH values of 5.1 and 6.1, indicating that PG-3 was effective at inhibiting S. mutans even under slightly acidic conditions. The glass particle with 42.7 mol% Zn may be useful for developing smart antibacterial restoratives that contribute to the prevention of diseases such as caries on root surfaces with lower acid resistance.

Incorporation of chlorhexidine in self-adhesive resin cements.

The aim of this study was to evaluate the maximum amount of chlorhexidine (CHX) that could be incorporated to self-adhesive resin cements to add antibacterial effect without affecting the physical properties. The CHX was incorporated into a commercial self-adhesive resin cement at mass fractions of 0.5-15 wt%, and the CHX-release profile, antibacterial effect, flexural and bond strengths of experimental cements were evaluated. Increasing the CHX content from 5 to 15 wt% resulted in a higher released concentration of CHX. In agar diffusion tests, experimental cements containing 5, 10, and 15 wt% CHX produced inhibition zones against oral bacteria. In flexural strength and shear bond strength to dentin, no significant reduction was observed with the incorporation of 5 wt% CHX. This in vitro study suggests that the addition of 5 wt% CHX yielded an antibacterial self-adhesive cement and had no adverse effect on the flexural and shear bond strengths.

Poly(lactic acid/caprolactone) bilayer membrane blocks bacterial penetration.

BACKGROUND AND OBJECTIVE: The clinical outcomes of guided tissue regeneration (GTR) or guided bone regeneration (GBR) procedures can be impaired if a bacterial infection develops at the surgical site. Membrane exposure is one of the causes of the onset of bacterial infection. Previously, we have fabricated a poly(lactic acid/caprolactone) (PLCL) bilayer membrane composed of a porous layer and a compact layer. The compact layer acts as a barrier against connective tissue and epithelial cells, and we hypothesized that it could also be an effective barrier against bacterial cells. The objective of this study was to evaluate the ability of the PLCL bilayer membrane to block bacterial cell penetration, which would be useful for preventing postoperative infections. METHODS: Porphyromonas gingivalis, Streptococcus mutans, and multispecies bacteria collected from human saliva were used in this study. Bacteria were seeded directly on the compact layer of a PLCL bilayer membrane, and bacterial adhesion to the membrane, as well as penetration into the membrane's structure, were assessed. Bacterial adhesion was evaluated by the number of colonies formed at 6, 24, and 72 h, and penetration was observed using a scanning electron microscope at 24 and 72 h. Commercially available membranes, composed of poly(lactic-co-glycolic acid) or type I collagen, were used as controls. RESULTS: P. gingivalis, S. mutans, and the multispecies bacteria obtained from human saliva adhered onto all the membranes after only 6 h of incubation. However, fewer adherent cells were observed for the PLCL bilayer membrane compared with the controls for all experimental periods. The PLCL membrane was capable of blocking bacterial penetration, and no bacterial cells were observed in the structure. In contrast, bacteria penetrated both the control membranes and were observed at depths of up to 80 µm after 72 h of incubation. CONCLUSION: Membrane characteristics may influence how bacterial colonization occurs. The PLCL membrane had reduced bacterial adhesion and blocked bacterial penetration, and these characteristics could contribute to a favorable outcome for regenerative treatments. In the event of membrane exposure at GTR/GBR surgical sites, membranes with an efficient barrier function, such as the PLCL bilayer membrane, could simplify the management of GTR/GBR complications.

Evaluation of the long-term antibiofilm effect of a surface coating with dual functionality of antibacterial and protein-repellent effects.

The provision of antibacterial properties to resinous restorative/reconstructive materials by incorporating polymerizable bactericides such as 12-methacryloyloxydodecylpyridinium bromide (MDPB) has been attempted. Previously, MDPB was combined with 2-methacryloyloxyethyl phosphorylcholine (MPC) to fabricate a copolymer coating to increase antibacterial effectiveness by protein repelling. In this study, we assessed the longevity of the protein-repelling, antibacterial, and antibiofilm effects of the MDPB-MPC copolymer. After 28 days of water immersion, MPC-containing copolymers exhibited lower adsorption of bovine serum albumin and salivary proteins; after 24 h of incubation, MDPB-containing copolymers demonstrated antibacterial effects against Streptococcus mutans. The copolymer containing both MDPB and MPC showed thinner biofilm formation with a higher percentage of membrane-compromised bacteria than control. The results were consistent with those before aging, indicating the long-lasting antibacterial, protein-repellent, and antibiofilm effects of this copolymer. The durable copolymer developed in this study can be applied to dental resins to control bacteria in the oral environment.

Physical properties and wear behavior of CAD/CAM resin composite blocks containing S-PRG filler for restoring primary molar teeth.

OBJECTIVES: This study aimed to develop computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite blocks (RCBs) containing surface pre-reacted glass-ionomer (S-PRG) filler for primary molar teeth and evaluate their physical properties and wear resistance. METHODS: Experimental CAD/CAM RCBs containing S-PRG filler for primary molar teeth (EB), a commercial CAD/CAM RCB (HC), two resin composites for primary teeth (BKP and BKZ) and one for permanent teeth (BⅡ) were used. Hardness tests, three-point bending tests, fracture toughness tests, and water absorption tests were conducted. Wear tests were conducted for these materials and stainless steel crowns (SSCs). RESULTS: The Vickers hardness of EB was lower than that of HC (p < 0.05), and there was no significant difference among BKZ, BKP, and BⅡ (p > 0.05). After 1 week of water immersion, EB and HC showed greater flexural strength than the other materials (p < 0.05). EB showed greater fracture toughness than the other materials (p < 0.05). The water absorption of EB was lower than that of HC, BKZ, and BKP (p < 0.05), and greater than that of BⅡ (p < 0.05). Antagonist wear was significantly smaller in EB than in HC and BⅡ (p < 0.05), and significantly greater than in BKZ (p < 0.05). Antagonist wear could not be measured in SSC because of excessive wear that was out of range of the surface roughness tester. SIGNIFICANCE: The CAD/CAM RCBs containing S-PRG filler for primary molar teeth developed in this study demonstrated adequate physical properties and wear performance, suggesting that they are suitable for restoration of primary molar teeth and could function in place of SSCs.

Establishment of novel in vitro culture system with the ability to reproduce oral biofilm formation on dental materials.

Intensive research has been conducted with the aim of developing dental restorative/prosthetic materials with antibacterial and anti-biofilm effects that contribute to controlling bacterial infection in the oral cavity. In situ evaluations were performed to assess the clinical efficacy of these materials by exposing them to oral environments. However, it is difficult to recruit many participants to collect sufficient amount of data for scientific analysis. This study aimed to assemble an original flow-cell type bioreactor equipped with two flow routes and assess its usefulness by evaluating the ability to reproduce in situ oral biofilms formed on restorative materials. A drop of bacterial suspension collected from human saliva and 0.2% sucrose solution was introduced into the assembled bioreactor while maintaining the incubation conditions. The bioreactor was able to mimic the number of bacterial cells, live/dead bacterial volume, and volume fraction of live bacteria in the in situ oral biofilm formed on the surface of restorative materials. The usefulness of the established culture system was further validated by a clear demonstration of the anti-biofilm effects of a glass-ionomer cement incorporating zinc-releasing glasses when evaluated by this system.

Antibacterial effects and physical properties of a glass ionomer cement containing BioUnion filler with acidity-induced ability to release zinc ion.

BioUnion filler is a bioactive glass particle that releases Zn2+ in an acidic environment. In this study, the ion release, antibacterial, and physical properties of a glass ionomer cement (GIC) incorporating BioUnion filler (CA) were assessed in vitro. The concentration of Zn2+ released from CA into acetic acid was higher than that released into water and its minimum inhibitory concentrations against six oral bacterial species. Moreover, the concentration of Zn2+-release was maintained during all the seven times it was exposed to acetic acid. Compared to a conventional cement and resin composite, CA significantly inhibited the growth of oral bacteria and hindered their adhesion on the material surface. Thus, our study outcomes show that the release of Zn2+ from CA in the acidic environment does not affect its compressive strength.

Development of endodontic sealers containing antimicrobial-loaded polymer particles with long-term antibacterial effects.

OBJECTIVE: The objective of this study is to prepare new dental resins with a long-lasting antimicrobial activity. Specifically, this study evaluates an approach for controlling infection in root canals using sealers containing polyhydroxyethyl methacrylate trimethylolpropane trimethacrylate (polyHEMA/TMPT) particles loaded with cetylpyridinium chloride (CPC). In addition, the physical properties of sealers containing CPC-loaded polyHEMA/TMPT particles (CLP) are determined. METHODS: PolyHEMA/TMPT particles with 10 (10%-CLP) and 25wt.% CPC (25%-CLP) with different particle sizes were fabricated and incorporated in HEMA-based sealers. CPC-release profiles were evaluated over 14 days of immersion in water, followed by 14 days of storage and 14 days of water immersion. The antibacterial activity of these sealers against Enterococcus faecalis in dentinal tubules was assessed using a root-canal-infection model. Their sealing abilities were evaluated by fluid filtration and physical properties were tested according to the ISO 6876 standard. The long-term antibacterial activity of the cured sealer containing 25%-CLP (∼21µm particle diameter) was re-assessed after 1 year of storage. RESULTS: After 28 days of immersion, 25%-CLP exhibited a higher and sustained CPC release unlike 10%-CLP. Residual bacteria in root dentinal tubules were eradicated by obturation with 25%-CLP-containing sealers. The incorporation of 25%-CLP (∼21µm) had no adverse effects on the sealing ability and physical properties of the sealer and resulted in long-term antibacterial activity. SIGNIFICANCE: The incorporation of CPC-loaded particles in HEMA resins yielded endodontic sealers with long-term bactericidal activity against E. faecalis in root canals. These sealers can potentially be used to prevent recurrent apical periodontitis.

Evaluation of ion release and the recharge ability of glass-ionomer cement containing BioUnion filler using an in vitro saliva-drop setting assembly.

OBJECTIVE: A glass-ionomer cement (GIC) containing BioUnion filler has been reported to release Zn2+ under acidic conditions and to inhibit oral bacteria on its surface. However, previous results are based on in vitro experiments under static conditions. This study aimed to assemble an in vitro saliva-drop setting to simulate in vivo conditions of the oral cavity and to investigate the ion releasing and recharging properties of the GIC containing BioUnion filler. METHODS: The effective concentrations of Zn2+ and F- against Streptococcus mutans and saliva-derived multi-species biofilms were determined. Artificial saliva was dropped on the GIC containing BioUnion filler using the in vitro saliva-drop setting assembly and was periodically replaced with acetic acid. Ion release/recharge properties were investigated by measuring the release concentrations of Zn2+ and F-. RESULTS: The concentration of Zn2+ released from the BioUnion filler-containing GIC during seven days with repeated exposure to acid could be maintained at the level to inhibit S. mutans and saliva-derived multi-species biofilm formation. Moreover, the BioUnion filler-containing GIC could be recharged with Zn2+ and F- by the application of a tooth gel containing Zn2+ and F-. The release concentration of Zn2+ after recharging was significantly higher than the effective concentration of Zn2+ to hinder S. mutans and saliva-derived multi-species biofilm formation on material surfaces. SIGNIFICANCE: The GIC containing BioUnion filler was shown to have the potential to inhibit biofilm formation in the oral cavity. In addition, recharging Zn2+ and F- would further enhance the effect of the GIC containing BioUnion filler.

Evaluation of human pulp tissue response following direct pulp capping with a self-etching adhesive system containing MDPB.

This study evaluated the human pulp tissue response following direct pulp capping with Clearfil Protect Bond (CPB) self-etching adhesive containing an antibacterial monomer MDPB. The pulps of third molar teeth were exposed by the removal of carious tissue. In an experimental group, CPB was applied to the exposed pulp and dentin. In the control groups, Clearfil SE Bond (CSE) or calcium hydroxide-based cement (CH) was applied to the exposed pulp surfaces. All teeth were filled with resin composite, extracted after 90 days, and the pulp responses were histologically analyzed. No severe inflammation or soft tissue disorganization was observed in CPB and CH groups. CSE group exhibited a disorganized odontoblastic layer and severe inflammatory infiltration. No hard tissue formation was observed in CSE group, and CH formed more of a hard tissue formation than CPB. CPB induced an acceptable healing response when directly applied to exposed pulps with bacterial contamination.

Antibacterial activities and mineral induction abilities of proprietary MTA cements.

Mineral trioxide aggregate (MTA) cements are used in direct pulp capping and many other applications, and several types of these products have been commercialized. The aim of this study was to examine the antibacterial effects and mineral induction abilities of three conventional MTA cements and one resin-modified MTA cement. Agar diffusion tests revealed that, after setting, all four cements exhibited little antibacterial effects against Enterococcus faecalis and Streptococcus mutans, with no significant differences among the materials. After 24 h, E. faecalis and S. mutans suspensions incubated in the presence of each cement did not exhibit reduced numbers of viable bacteria, compared with those same bacterial suspensions incubated without any cement; this indicated that none of the cements inhibited bacterial growth. Furthermore, the resin-modified MTA cement exhibited lower mineral induction ability, compared with that of the three conventional MTA cements.

FGF-2 release and bonding/physical properties of 4-META/MMA-based adhesive resins incorporating small FGF-2-loaded polymer particles.

OBJECTIVES: Non-biodegradable particles comprising hydroxyethyl methacrylate (HEMA) and trimethylolpropane trimethacrylate (TMPT) have been reported as useful carriers for fibroblast growth factor-2 (FGF-2). They have also been successfully incorporated into the 4-[2-(methacryloyloxy)ethoxycarbonyl]phthalic anhydride/methyl methacrylate-tri-n-butyl borane (4-META/MMA-TBB) resin to promote tissue regeneration. However, smaller particles are required to obtain restorative materials acceptable for clinical use. The aim of this study was to investigate the ability of the 4-META/MMA-TBB resin that comprises small FGF-2-loaded particles to release FGF-2 and promote cell proliferation. In addition, the bonding and physical properties of the experimental resin were evaluated. METHODS: The small particles loaded with FGF-2 were newly fabricated and incorporated into the commercial 4-META/MMA-TBB resin. Release profiles of FGF-2 from the experimental resins were assessed, and the cell proliferation cultured with the eluate was evaluated. The bonding and physical properties of the resins were evaluated using shear bond strength and three-point bending tests, and by measuring the curing time, water absorption, and water dissolution. RESULTS: Sustained release of FGF-2 from the experimental resins for two weeks was observed, and the released FGF-2 was demonstrated to promote cell proliferation. All bonding and physical properties of the 4-META/MMA-TBB resins were found acceptable for clinical use. SIGNIFICANCE: The small FGF-2-loaded particles incorporated into the 4-META/MMA-TBB resin had the same abilities to release FGF-2 and proliferate cells, as those exhibited by the conventionally sized particles. In addition, there were no adverse influences on bonding and physical properties, suggesting that the bioactive adhesive resin was acceptable for clinical use.

Development of novel surface coating composed of MDPB and MPC with dual functionality of antibacterial activity and protein repellency.

Resin-based reconstructive/restorative materials with antibacterial effects are potentially useful for preventing dental and oral diseases. To this end, the immobilization of an antibacterial component on the surface of a resin by incorporating polymerizable bactericide such as a quaternary ammonium compound-monomer 12-methacryloyloxydodecylpyridinium bromide (MDPB) is an effective technique. However, the effectiveness of immobilized bactericide is reduced by salivary protein coverage. We address this issue by utilizing 2-methacryloyloxyethyl phosphorylcholine (MPC) polymer, which exhibits protein repellency, with MDPB to fabricate a novel copolymer, which served as a surface coating on a methacrylate-based resin. This coating provided a more hydrophilic surface than that provided by MDPB coating and reduced the adsorption of bovine serum albumin and salivary protein. To evaluate bacterial growth on the contact surface, Streptococcus mutans suspension was placed on the coated specimen. After 24-h incubation, MDPB/MPC copolymer exhibited killing effects against S. mutans. Moreover, confocal laser scanning microscopy and scanning electron microscopy were used to evaluate biofilm formation after 48-h incubation in S. mutans suspension, which revealed sparse biofilm and dead bacteria in biofilm on the surface coated with MDPB/MPC. Overall, the proposed surface coating on dental resins exhibited protein-repellent ability and inhibitory effects against bacteria and oral biofilms.

Fabrication of novel poly(lactic acid/caprolactone) bilayer membrane for GBR application.

OBJECTIVE: Guided bone regeneration (GBR) often involves the use of membranes as barriers for soft tissues. Commercially available membranes, however, do not possess an adequately low degradation rate, resulting in limited barrier function. The purpose of this study was to develop and assess the physicochemical and biological characteristics of a novel poly(l-lactic acid/caprolactone) (PLCL) bilayer membrane and determine its usefulness for GBR application. METHODS: The experimental bilayer membrane was prepared via a two-step freezing and lyophilization process with a PLCL solution. Next, the PLCL membrane was investigated regarding tensile strength, surface roughness, in vitro degradation and clinical operability. In addition, cell proliferation and differentiation were investigated on each layer of the experimental membrane. For all experiments, a commercially available poly(lactic-co-glycolic) acid membrane was used as a control. RESULTS: In vitro analysis of the PLCL bilayer membrane revealed suitable mechanical strength combined with high breaking strain, which contributed to membrane operability. In addition, the PLCL bilayer membrane had enhanced stability compared to the commercial control due to its slower degradation, and was capable of supporting cell growth and osteogenic differentiation. SIGNIFICANCE: The current study confirmed that the PLCL membrane possessed a high biocompatibility and slow degradation rate that contributes to prolonged barrier function and bone regeneration. Altogether, it was considered that the PLCL bilayer membrane developed in this study was applicable for GBR treatment.

Acidity-induced release of zinc ion from BioUnionTM filler and its inhibitory effects against Streptococcus mutans.

BioUnion filler incorporated into restorative/coating materials is a new bio-functional glass powder. The most unique function of BioUnion filler is its ability to release Zn2+ in acidic environments. In this study, the ion release profile of BioUnion filler under acidic conditions and its antibacterial effects against Streptococcus mutans were evaluated. The concentrations of Zn2+ released from BioUnion fillers into acetic acids were greater than those released into water. S. mutans inhibition by BioUnion fillers was greater with sucrose than without sucrose, reflecting a decrease in suspension pH in response to the addition of sucrose. Exposure to acids increased Zn2+ release from BioUnion fillers, and the fillers after repeated exposure to acids demonstrated inhibitory effects against S. mutans. These findings suggest that BioUnion filler accelerated the release of Zn2+ under acidic conditions, which induced bactericidal/inhibitory effects against S. mutans.

Cutting-edge filler technologies to release bio-active components for restorative and preventive dentistry.

Advancements in materials used for restorative and preventive treatment is being directed toward "bio-active" functionality. Incorporation of filler particles that release active components is a popular method to create bio-active materials, and many approaches are available to develop fillers with the ability to release components that provide "bio-protective" or "bio-promoting" properties; e.g. metal/calcium phosphate nanoparticles, multiple ion-releasing glass fillers, and non-biodegradable polymer particles. In this review paper, recent developments in cutting-edge filler technologies to release bio-active components are addressed and summarized according to their usefulness and functions, including control of bacterial infection, tooth strengthening, and promotion of tissue regeneration.